尼龙6塑料原料尼龙6高温、高强度、阻燃、增韧、抗寒-40摄氏度

尼龙6塑料原料尼龙6

产品详细信息‍

尼龙PA6

疲劳强度、刚度和耐热性低于尼龙66，但具有良好的弹性，并具有更好的减振降噪能力。白色

尼龙PA6应用：轻载，中温（80-100）无润滑或少润滑

尼龙PA6塑料原料收缩率1.0%浅黄色至琥珀色透明固体，燃烧

尼龙PA6塑料材料坚硬，耐磨，耐疲劳，耐油，耐水，具有高结晶性能。它们具有优异的机械性能，刚度低于金属，但比强度高于金属，聚甲醛含量低，但热稳定性差，产品一般只能在80-100度下使用，PA6弹性好，冲击强度高，吸水率高。PA66具有高强度和良好的耐磨性。PA610与PA66相似，但吸收性和刚性较差。PA1010半透明，吸水率低，耐寒性好

1。它很容易吸收水分，成型前必须干燥。如果吸湿后流动性降低，则容易出现气泡和银丝

2。流动性好，容易溢出和浇铸，因此必须控制成型温度，应使用专用喷嘴，并应选择小间隙

3。成型范围和收缩率大，方向性明显，容易出现缩孔、凹痕和变形

4。熔融尼龙的冷却速度对结晶度有很大影响，对塑料件的结构和性能有很大影响，因此应适当控制模具温度。在20-90度范围内，如果模具温度较低，则可能出现缩孔和低结晶度

是专业的pa6塑料原料尼龙6制造商之一，您可以从我们工厂以优惠的价格订购高品质的pa6塑料原料尼龙6

PA6 Plastic Raw Material Nylon6

High temperature,
high strength,
fire retardant，
Toughening,
anti-cold -40 degrees centigrade.

PA6 Plastic Raw Material Nylon6

Product Details

‍PA6 Plastic raw Material Nylon6

Nylon PA6

Fatigue strength, rigidity, and heat resistance are lower than nylon 66, but have good elasticity, and have better vibration and noise reduction capabilities. White

Nylon PA6 application: light load, medium temperature (80-100) no lubrication or less lubrication

Pa6 plastic raw material shrinkage rate 1.0% light yellow to amber transparent solid, burning

Pa6 plastic materials are hard, wear-resistant, fatigue-resistant, oil-resistant, water-resistant, and have high crystallization properties. They have excellent mechanical properties, their stiffness is lower than that of metals, but their specific strength is higher than that of metals. , POM is low, but thermal stability is poor, products generally can only be used at 80-100 degrees PA6 has good elasticity, high impact strength, and high water absorption. PA66 has high strength and good wear resistance. PA610 is similar to PA66, but less absorbent and less rigid. PA1010 is translucent, with low water absorption and good cold resistance.

1. It is easy to absorb moisture and must be dried before molding. If the fluidity decreases after moisture absorption, air bubbles and silver threads are prone to appear.

2. Good fluidity, easy to overflow and cast, so the molding temperature must be controlled, special nozzles should be used, and small gaps should be selected.

3. The molding range and shrinkage rate are large, and the directionality is obvious, so shrinkage holes, dents and deformations are prone to occur.

4. The cooling rate of molten nylon has a great influence on the crystallinity, and has a significant impact on the structure and performance of the plastic parts, so the mold temperature should be properly controlled. In the range of 20-90 degrees, if the mold temperature is low, shrinkage cavities and low crystallinity are likely to occur.

Contactnowformoredetailsabout PA6 Plastic raw Material Nylon6.

is one of the professional pa6 plastic raw material nylon6 manufacturers, you can order high quality pa6 plastic raw material nylon6 at good price from our factory.